Pilot demonstration of cerium oxide coated anodes [electronic resource].
- Published:
- Washington, D.C. : United States. Dept. of Energy, 1992.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy. - Physical Description:
- Pages: (216 pages) : digital, PDF file
- Additional Creators:
- United States. Department of Energy
United States. Department of Energy. Office of Scientific and Technical Information - Access Online:
- www.osti.gov
- Summary:
- Cu cermet anodes were tested for 213 to 614 hours with an in-situ deposited CEROX coating in a pilot cell operated by Reynolds Manufacturing Technology Laboratory. At high bath ratio ([approximately]1.5) and low current density (0.5 A/cm[sup 2]), a [ge]1 mm thick dense CEROX coating was deposited on the anodes. At lower bath ratios and higher current density, the CEROX coating was thinner and less dense, but no change in corrosion rate was noted. Regions of low current density on the anodes and sides adjacent to the carbon anode sometimes had thin or absent CEROX coatings. Problems with cracking and oxidation of the cermet substrates led to higher corrosion rates in a pilot cell than would be anticipated from lab scale results.
- Subject(s):
- Note:
- Published through SciTech Connect.
10/01/1992.
"doe/id/12940-1"
"DE93002507"
Gregg, J.S.; Alcorn, T.R.; Frederick, M.S.; Shingler, M.J.
ELTECH Research Corp., Fairport Harbor, OH (United States) - Funding Information:
- FC07-90ID12940
View MARC record | catkey: 14395971