SALT FOG TEST OF SAM2X5 COATED STAINLESS STEEL CYLINDER [electronic resource].
- Washington, D.C. : United States. Dept. of Energy, 2007.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
- Physical Description:
- PDF-file: 11 pages; size: 0.5 Mbytes
- Additional Creators:
- Lawrence Berkeley National Laboratory, United States. Department of Energy, and United States. Department of Energy. Office of Scientific and Technical Information
- Restrictions on Access:
- Free-to-read Unrestricted online access
- A salt fog test of an iron-based amorphous metal, SAM2X5, coated Type 316L stainless steel (SS316L) cylinder was made. The cylinder was 30-inch diameter by 88-inch long, and 3/8-inch thick. One end was welded shut with a SS316L end cap before coating. The body of the cylinder and the end cap were both coated. The cylinder was coated with SAM2X5 by the HVOF thermal spray process. The coating thickness was 0.015-inch to 0.019-inch thick. The cylinder was tested in a horizontal position. Also included in the test for reference purposes were five coupons (2-inch x 2-inch x 1/8-inch) of uncoated Type 1018 carbon steel (1018CS). The test used an abbreviated form of GM 9540P. Each cycle was 6 hours in duration and the cylinder and reference samples were exposed to a total of eight cycles. The cylinder was in relatively good condition after the test. Along the body of the cylinder only two pinpoint spot sized signs of rust were seen. The 1018CS reference specimens were extensively rusted.
- Report Numbers:
- E 1.99:ucrl-conf-230612
- Other Subject(s):
- Published through SciTech Connect.
Presented at: Materials Science and Technology 2007 Conference, MS&T?07, Detroit, MI, United States, Sep 16 - Sep 20, 2007.
Day, S D; Choi, J; Rebak, R B; Lian, T; Aprigliano, L F.