Actions for On the Relationship of Magnetocrystalline Anisotropy and Stoichiometry in Epitaxial L1{sub 0} CoPt(001) and FePt(001) Thin Films [electronic resource].

Email RIS file
Bookmark
Report an Issue

On the Relationship of Magnetocrystalline Anisotropy and Stoichiometry in Epitaxial L1{sub 0} CoPt(001) and FePt(001) Thin Films [electronic resource].

Published
Washington, D.C. : United States. Dept. of Energy, 2004.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
Physical Description
vp : digital, PDF file
Additional Creators
Stanford Linear Accelerator Center, United States. Department of Energy, and United States. Department of Energy. Office of Scientific and Technical Information
Access Online

Availability

I Want It
I Want It

Finding items...

Restrictions on Access
Free-to-read Unrestricted online access
Summary
Two series of epitaxial CoPt and FePt films, with nominal thicknesses of 42 or 50 nm, were prepared by sputtering onto single crystal MgO(001) substrates in order to investigate the chemical ordering and the resultant magnetic properties as a function of alloy composition. In the first series, the film composition was kept constant, while the substrate temperature was increased from 144 to 704 C. In the second series the substrate temperature was kept constant at 704 C for CoPt and 620 C for FePt, while the alloy stoichiometry was varied in the nominalrange of 40-60 at% Co(Fe). Film compositions and thicknesses were measured via Rutherford backscattering spectrometry. The lattice and long-range order parameter for the L1₀ phase were obtained for both sets of films using x-ray diffraction. The room-temperature magnetocrystalline anisotropy constants were determined for a subset of the films using torque magnetometry. The order parameter was found to increase with increasing temperature, with ordering occurring more readily in FePt when compared with CoPt. A perpendicular anisotropy developed in CoPt for substrate temperatures above 534 C and in FePt above 321 C. The structure and width of the magnetic domains in CoPt and FePt, as seen by magnetic force microscopy, also demonstrated an increase in magnetic anisotropy with increasing temperature. For the films deposited at the highest temperatures (704 C for CoPt and 620 C for FePt), the order parameter reached a maximum near the equiatomic composition, whereas the magnetocrystalline anisotropy increased as the concentration of Co or Fe was increased from below to slightly above the equiatomic composition. It is concluded that non-stoichiometric L1₀ CoPt and FePt, with a slight excess of Co or Fe, are preferable for applications requiring the highest anisotropies.
Report Numbers
E 1.99:slac-pub-10614
slac-pub-10614
Subject(s)
Other Subject(s)
Note
Published through SciTech Connect.
08/10/2004.
"slac-pub-10614"
Barmak, K.
Type of Report and Period Covered Note
Topical;
Funding Information
AC03-76SF00515
View MARC record | catkey: 14447823