Actions for Final Report, Volume 1, Metallurgical Evaluation of Cast Duplex Stainless Steels and their Weldments [electronic resource].

Email RIS file
Bookmark
Report an Issue

Final Report, Volume 1, Metallurgical Evaluation of Cast Duplex Stainless Steels and their Weldments [electronic resource].

Published
Washington, D.C. : United States. Dept. of Energy. Office of Environmental Management, 2005.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
Physical Description
11.5 : digital, PDF file
Additional Creators
University of Tennessee, Knoxville, United States. Department of Energy. Office of Environmental Management, United States. Department of Energy. Office of Conservation and Renewable Energy. Office of Industrial Technologies, and United States. Department of Energy. Office of Scientific and Technical Information
Access Online

Availability

I Want It
I Want It

Finding items...

Restrictions on Access
Free-to-read Unrestricted online access
Summary
Duplex stainless steels (DSS) are being specified for chloride containing environments due to their enhanced pitting and stress corrosion cracking resistance. They exhibit improved corrosion performance over the austenitic stainless steels. Duplex stainless steels also offer improved strength properties and are available in various wrought and cast forms. Selected grades of duplex stainless steel castings and their welds, in comparison with their wrought counterparts, were evaluated, regarding corrosion performance and mechanical properties and weldability. Multiple heats of cast duplex stainless steel were evaluated in the as-cast, solution annealed (SA) static cast and SA centrifugal cast conditions, while their wrought counterparts were characterized in the SA condition and in the form of as-rolled plate. Welding, including extensive assessment of autogenous welds and a preliminary study of composite welds (shielded metal arc weld (SMAW)), was performed. The evaluations included critical pitting temperature (CPT) testing, intergranular corrosion (IGC) testing, ASTM A923 (Methods A, B and C), Charpy impact testing, weldability testing (ASTM A494), ferrite measurement and microstructural evaluations. In the study, the corrosion performances of DSS castings were characterized and assessed, including the wrought counterparts for comparison. The evaluation filled the pore of lack of data for cast duplex stainless steels compared to wrought materials. A database of the pitting corrosion and IGC behavior of cast and wrought materials was generated for a greater depth of understanding for the behavior of cast duplex stainless steel. In addition, improved evaluation methods for DSS castings were developed according to ASTM A923, A262, G48 and A494. The study revealed that when properly heat treated according to the specification, (1) DSS castings have equal or better pitting and intergranular corrosion resistance than their wrought counterparts; (2) Welding reduces the pitting and intergranular corrosion resistance for both the wrought and cast duplex alloys; (3) Castings generally have better toughness than their wrought counterparts in the temperature range of -80 C to +20 C; (4) All shield metal arc (SMA) test welds in DSS castings, with recommended or over matching filler metal, indicate that welding is not a significant factor when considering DSS applications.
Report Numbers
E 1.99:doe/id/13975-1
doe/id/13975-1
Subject(s)
Other Subject(s)
Note
Published through SciTech Connect.
09/30/2005.
"doe/id/13975-1"
Wen, Songqing; Lundin, Carl, W.; Batten, Greg, W.
Type of Report and Period Covered Note
Final; 10/01/2000 - 09/30/2005
Funding Information
FC36-00ID13975
View MARC record | catkey: 14448208