Interfacial debonding versus fiber fracture in fiber-reinforced ceramic composites [electronic resource].
- Washington, D.C. : United States. Dept. of Energy. Office of Energy Research, 1998.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
- Physical Description:
- 6 pages : digital, PDF file
- Additional Creators:
- Oak Ridge National Laboratory
United States. Department of Energy. Office of Energy Research
United States. Department of Energy. Office of Scientific and Technical Information
- Toughening of fiber-reinforced ceramic composites by fiber pullout relies on debonding at the fiber/matrix interface prior to fiber fracture when composites are subjected to tensile loading. The criterion of interfacial debonding versus crack penetration has been analyzed for two semi-infinite elastic plates bonded at their interface. When a crack reaches the interface, the crack either deflects along the interface or penetrates into the next layer depending upon the ratio of the energy release rate for debonding versus that for crack penetration. This criterion has been used extensively to predict interfacial debonding versus fiber fracture for a crack propagating in a fiber-reinforced ceramic composite. Two modifications were considered in the present study to address the debonding/fracture problem. First, the authors derived the analysis for a strip of fiber, which had a finite width and was sandwiched between two semi-infinite plates of matrix. It was found that the criterion of interfacial debonding versus fiber fracture depended on the fiber width. Second, a bridging fiber behind the crack tip was considered where the crack tip initially circumvented the fiber. Subsequent to this, either the interface debonded or the fiber fractured. In this case, the authors have considered a bridging-fiber geometry to establish a new criterion.
- Published through SciTech Connect.
1. China international conference in high-performance ceramics, Beijing (China), 31 Oct - 3 Nov 1998.
Becher, P.F.; Hsueh, C.H.; He, M.Y.
- Funding Information:
View MARC record | catkey: 14449958