Physical and mechanical properties of cast 17-4 PH stainless steel [electronic resource].
- Washington, D.C. : United States. Dept. of Energy, 1981.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
- Physical Description:
- Pages: 63 : digital, PDF file
- Additional Creators:
- Sandia National Laboratories
United States. Department of Energy
United States. Department of Energy. Office of Scientific and Technical Information
- The physical and mechanical properties of an overaged 17-4 PH stainless steel casting have been examined. The tensile and compressive properties of cast 17-4 PH are only influenced to a slight degree by changing test temperature and strain rate. However, both the Charpy impact energy and dynamic fracture toughness exhibit a tough-to-brittle transition with decreasing temperature - this transition being related to a change in fracture mode from ductile, dimple to cleavage-like. Finally, although the overaged 17-4 PH casting had a relatively low room temperature Charpy impact energy when compared to wrought 17-4 PH, its fracture toughness was at least comparable to that of wrought 17-4 PH. This observation suggests that prior correlations between Charpy impact energies and fracture toughness, as derived from wrought materials, must be approached with caution when applied to cast alloys.
- Published through SciTech Connect.
Rack, H. J.
- Funding Information:
View MARC record | catkey: 14462664