Metallurgical examination of gun barrel screws [electronic resource].
- Washington, D.C. : United States. Dept. of Energy, 1996.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
- Physical Description:
- 32 pages : digital, PDF file
- Additional Creators:
- United States. Department of Energy and United States. Department of Energy. Office of Scientific and Technical Information
- Restrictions on Access:
- Free-to-read Unrestricted online access
- The examination was conducted to determine the extent of degradation that had occurred after a series of firings; these screws prevent live rounds of ammunition from being loaded into the firing chamber. One concern is that if the screw tip fails and a live round is accidentally loaded into the chamber, a live round could be fired. Another concern is that if the blunt end of the screw begins to degrade by cracking, pieces could become small projectiles during firing. All screws used in firing 100 rounds or more exhibited some degree degradation, which progressively worsened as the number of rounds fired increased. (SEM, metallography, x-ray analysis, and microhardness were used.) Presence of cracks in these screws after 100 fired rounds is a serious concern that warrants the discontinued use of these screws. The screw could be improved by selecting an alloy more resistant to thermal and chemical degradation.
- Report Numbers:
- E 1.99:y/dv--1401
- Other Subject(s):
- Published through SciTech Connect.
Bird, E.L.; Clift, T.L.
Oak Ridge Y-12 Plant, TN (United States)