Subtask 12F4 [electronic resource] : Effects of neutron irradiation on the impact properties and fracture behavior of vanadium-base alloys

Published: Argonne, Ill. : Argonne National Laboratory, 1995.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
Physical Description: pages 147-155 : digital, PDF file
Additional Creators: Argonne National Laboratory and United States. Department of Energy. Office of Scientific and Technical Information

Access Online

www.osti.gov

Availability

Finding items...

Restrictions on Access

Free-to-read Unrestricted online access

Summary

Up-to-date results on the effects of neutron irradiation on the impact properties and fracture behavior of V, V-Ti, V-Cr-Ti and V-Ti-Si alloys are presented in this paper, with an emphasis on the behavior of the U.S. reference alloys V-4Cr-4Ti containing 500-1000 wppm Si. Database on impact energy and cluctile-brittle transition temperature (DBTT) has been established from Charpy impact tests of one-third-size specimens irradiated at 420°C-600°C up to ≈50 dpa in lithium environment in fast fission reactors. To supplement the Charpy impact tests fracture behavior was also characterized by quantitative SEM fractography on miniature tensile and disk specimens that were irradiated to similar conditions and fractured at -196°C to 200°C by multiple bending. For similar irradiation conditions irradiation-induced increase in DBTT was influenced most significantly by Cr content, indicating that irradiation-induced clustering of Cr atoms takes place in high-Cr (Cr ≥ 7 wt.%) alloys. When combined contents of Cr and Ti were ≤10 wt.%, effects of neutron irradiation on impact properties and fracture behavior were negligible. For example, from the Charpy-impact and multiple-bend tests there was no indication of irradiation-induced embrittlement for V-5Ti, V-3Ti-1Si and the U.S. reference alloy V-4Cr-4Ti after irradiation to ≈34 dpa at 420°C to 600°C, and only ductile fracture was observed for temperatures as low as -196°C. 14 refs., 8 figs., 1 tab.

Report Numbers

E 1.99:anl/fpp/tm--287
E 1.99: iter/us--95/iv-mat-10
iter/us--95/iv-mat-10
anl/fpp/tm--287

Subject(s)

Other Subject(s)

Note

Published through SciTech Connect.
03/01/1995.
"anl/fpp/tm--287"
" iter/us--95/iv-mat-10"
"DE96000984"
Smith, D.L.; Loomis, B.A.; Chung, H.M.

View MARC record | catkey: 14745302