Actions for Erosion and redeposition experiments in the PISCES facility [electronic resource].

Email RIS file
Bookmark
Report an Issue

Erosion and redeposition experiments in the PISCES facility [electronic resource].

Published
Los Angeles, Calif. : University of California, Los Angeles, 1986.
Oak Ridge, Tenn. : Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy.
Physical Description
Pages: 32 : digital, PDF file
Additional Creators
University of California, Los Angeles and United States. Department of Energy. Office of Scientific and Technical Information
Access Online

Availability

I Want It
I Want It

Finding items...

Restrictions on Access
Free-to-read Unrestricted online access
Summary
The modification of surfaces during exposure to plasma bombardment is a critical issue in the development of limiter and wall materials for fusion confinement experiments. Controlled studies of the erosion and redeposition of materials during high flux and fluence plasma exposure are now possible in the PISCES facility. PISCES is a continuously operating plasma device which has achieved hydrogen plasma densities of over 10/sup 13/ cm/sup -3/ and electron temperatures of 5 to 24 eV over large areas. Ion fluxes of 10/sup 17/ to 10/sup 19/ cm/sup -2/ sec/sup -1/ and fluences of up to 10/sup 23/ cm/sup -2/ have been used to bombard biased samples inserted into the plasma. The plasma parameters can be selected to produce simple sputtering, or redeposition by the ionization and recycling of the sputtered target materials. Collaborative studies on the performance of Cu and Cu-Li alloys (with ANL), stainless steel (with SNLL), and graphite (with IPP at Garching, and SNLL) have been undertaken. Surface topography modification is always observed after a sufficient fluence is achieved. The net erosion rate is significantly lower during redeposition than one would expect from classical sputtering yields. The transport and deposition of different materials by the plasma to the samples during redeposition conditions results in greatly modified surface composition and morphology. Chemical sputtering of graphite during low energy, high flux (>10/sup 18/ cm/sup -2/ sec/sup -1/) plasma bombardment is observed. Chemically formed hydrocarbons are relatively easily redeposited compared to sputtered carbon. The performance of these materials, the surface morphology evolution, and the characteristics of the redeposited materials are discussed.
Report Numbers
E 1.99:ucla/ppg-982
ucla/ppg-982
Subject(s)
Other Subject(s)
Note
Published through SciTech Connect.
05/01/1986.
"ucla/ppg-982"
"DE86015000"
Goebel, D.M.; Hirooka, Y.; Causey, R.A.; Conn, R.W.; Campbell, G.A.; Leung, W.K.; Pontau, A.E.; Bohdansky, J.; Wilson, K.L.; Bauer, W.
Funding Information
AS03-84ER52104
View MARC record | catkey: 14751789