Static tests were made on the compatibility of liquid fluorine with several nonmetallic materials at -3200 F and at pressures of 0 and 1500 pounds per square inch gage. The results are compared with those from previous work with gaseous fluorine at the same pressures, but at atmospheric temperature. In general, although environmental effects were not always consistent, reactivity was least with the low-temperature, low-pressure liquid fluorine. Reactivity was greatest with the warm, high-pressure gaseous fluorine. None of the liquids and greases tested was found to be entirely suitable for use in fluorine systems. Polytrifluorochloroethylene and N-43, the formula for which is (C4F9)3N, did not react with liquid fluorine at atmospheric pressure or 1500 pounds per square inch gage under static conditions, but they did react when injected into liquid fluorine at 1500 pounds per square inch gage; they also reacted with gaseous fluorine at 1500 pounds per square inch gage. While water did not react with liquid fluorine at 1500 pounds per square inch gage, it is known to react violently with fluorine under other conditions. The pipe-thread lubricant Q-Seal did not react with liquid fluorine, but did react with gaseous fluorine at 1500 pounds per square inch gage. Of the solids, ruby (Al2O3) and Teflon did not react under the test conditions. The results show that the compatibility of fluorine with nonmetals depends on the state of the fluorine and the system design.