Sliding Contact Bearings for Service to 700 C.
- Sliney, Harold E.
- Sep. 1996.
- Physical Description:
- 1 electronic document
- Restrictions on Access:
- Unclassified, Unlimited, Publicly available. and Free-to-read Unrestricted online access
- Cylindrical, sliding contact bearings made entirely of a self-lubricating powder metallurgy composite (PM212) or of super alloy shells lined with clad PM212 were tested in an oscillating mode at temperatures from 25 to 700 C. Tests of 100 hr duration or longer were conducted at a bearing unit load of 3.45 Mpa (500 psi). Shorter duration tests at various unit loads up to 24.1 Mpa (3500 psi) were also conducted. In comparison tests, bearings lubricated with PM212 had superior anti-wear characteristics compared to the baseline, unlubricated, super alloy bearings: no galling of PM212-lubricated bearings occurred, while severe surface damage including galling occurred, especially at high loads, during the baseline tests. A heat treatment procedure, which dimensionally stabilizes PM212 and thereby minimizes clearance changes during high temperature bearing operation, is described.
- NASA Technical Reports Server (NTRS) Collection.
- Document ID: 19970001430., Accession ID: 97N11245., NAS 1.15:107307., E-10396., and NASA-TM-107307.
- No Copyright.
View MARC record | catkey: 15649383