The composition and surface profiles of M-50 steel surfaces were measured after operation at high loads in a bearing contact simulator. An ester lubricant (trimethyolpropane triheptanoate) was used with and without various additives. Optical profiles were obtained + or - to 30 depth resolution with a phase-locked interference microscope in 10 micron diameter areas within and outside the wear tracks. Optical constants and surface film thickness were measured in the same areas with an electronic scanning ellipsometer. Film composition was measured with a scanning Auger electron spectrometer. It is concluded that metal oxide formation is accelerated within the wear tracks.