Evaluation of candidate Stirling engine heater tube alloys for 1000 hours at 760 C.

Author:
Misencik, J. A.
Published:
Nov 1, 1980.
Physical Description:
1 electronic document
Online Version

Availability

I Want It

Finding items...

Restrictions on Access:
Unclassified, Unlimited, Publicly available.
Free-to-read Unrestricted online access
Summary:
Six tubing alloys were endurance tested in a diesel fired, Stirling engine simulator materials test rig for 1000 hours of 760 C while pressurized at 17 to 21 MPa with either hydrogen or helium. The alloys tested were N 155, A 286, Incoloy 800, 19 9DL, Nitronic 40 and 316 stainless steel. The alloys were in the form of thin wall tubing. Hydrogen permeated rapidly through the tube walls of all six alloys when they were heated to 760 C. Helium was readily contained. Creep rupture failures occurred in four of the six alloys pressurized with hydrogen. Only two alloys survived the 1000 hour endurance test with no failures. Simultaneous exposure to either hydrogen or helium and the combustion environment did not seriously degrade the tensile strength of the six alloys in room temperature or 760 C tests after exposure. Decreases in room temperature ductility were observed and are attributed to aging rather than to hydrogen embrittlement in three of the alloys. However, there may be a hydrogen embrittlement effect in the N 155, 19 9DL, and Nitronic 40 alloys.
Other Subject(s):
Collection:
NASA Technical Reports Server (NTRS) Collection.
Note:
Document ID: 19810006553.
Accession ID: 81N15068.
E-548.
DOE/NASA/1040-18.
NASA-TM-81578.
Terms of Use and Reproduction:
No Copyright.
View MARC record | catkey: 15720431