Recent work at NASA Langley Research Center (LaRC) has concentrated on developing new polyimide resin systems for advanced aerospace applications that can be processed without the use of an autoclave. Polyimide composites are very attractive for applications that require a high strength to weight ratio and thermal stability. Vacuum assisted resin transfer molding (VARTM) has shown potential to reduce the manufacturing cost of composite structures. In VARTM, the fibrous preform is infiltrated on a rigid tool surface contained beneath a flexible vacuum bag. Both resin injection and fiber compaction are achieved under pressures of 101.3 KPa or less. Recent studies have demonstrated the feasibility of the VARTM process for fabrication of void free structures utilizing epoxy resin systems with fiber volume fractions approaching 60%. In this work, the VARTM process has been extended to the fabrication of composite panels from polyimide systems developed at the Langley Research Center. This work has focused on processing LARC(trademark) PETI-8 (Langley Research Center Phenylethynyl Terminated Imide- 8), an aromatic polyimide based on 3,3',4,4' -biphenyltetracarboxylic dianhydride, a 50:50 molar ratio of 3,4'-oxydianiline and 1,3-bis(3-aminophenoxy)benzene, with 4-phenylethynylphthalic anhydride as the endcapping agent. Various molecular weight versions were investigated to determine their feasibility of being processed by VARTM at elevated temperatures. An injection temperature of approximately 280 C was required to achieve the necessary viscosity (<5 Poise) for flow at VARTM pressures. Laminate quality and initial mechanical properties are presented for LARC(trademark) PETI-8 and 6k IM7 uniweave fabric.